Cr containing steel for welded structure

ABSTRACT

The present invention provides Cr-containing steel that has satisfactory levels in all of toughness, strength (hardness) and corrosion resistance of HAZ, and that is suitably used as parts for welded structures.  
     Specifically, the present invention provides Cr-containing steel used for a welded structure, the steel being featured or characterized by containing, by mass %, C: not more than 0.020%, Si: not more than 1.00%, Mn: 1.0 to 5.0%, P: not more than 0.050%, S: not more than 0.020%, Cr: 6.0 to 15.0%, Ni: not more than 1.0%, Al: not more than 0.100%, N: not more than 0.020%, and V: 0.03 to 0.30%, the balance consisting of Fe and unavoidable impurities, or further containing Cu: 0.10 to 2.00% or less and Mo: 0.40 to 3.00% or less, wherein an F or F′ value calculated by putting values of contents (mass %) of the respective components in the following formula (1) or (2) is not larger than 13.50:  
               F                 value     =     Cr   +     0.4   ×   Si     +     0.2   ×   Al     +     5   ×   P     -     0.4   ×   Mn     -     0.7   ×   Ni     -     35   ×   C     -     10   ×   N     +     10   ×   V               (   1   )                   F   ′                   value     =     Cr   +     0.6   ×   Mo     +     0.4   ×   Si     +     0.2   ×   Al     +     5   ×   P     -     0.4   ×   Mn     -     0.7   ×   Ni     -     0.6   ×   Cu     -     35   ×   C     -     10   ×   N     +     10   ×   V               (   2   )

TECHNICAL FIELD

[0001] The present invention relates to Cr-containing steel used for a welded structure, in particular, suitably used as members arranged around the tire attachment area in an automobile.

BACKGROUND ART

[0002] Hitherto, coated steel obtained by welding, machining and then coating plain steel has been primarily employed as members arranged around the tire attachment area in an automobile.

[0003] The members arranged around the tire attachment area in an automobile are required to have high strength for ensuring sufficient rigidity. Also, because those members are used as welded structure parts that are welded to a vehicle body, etc., they are required to have sufficient toughness and high strength in welding area, such as a bead and a welding-heat affected zone (abbreviated to “HAZ” hereinafter). Further, the members arranged around the tire attachment area in an automobile are located in positions where they are directly exposed to, e.g., splash water from the road surface, and hence are required to have superior corrosion resistance as well.

[0004] A welded bead has no problems because satisfactory levels of strength, toughness and corrosion resistance can be ensured by selecting a proper welding wire. However, characteristics of HAZ, such as strength, toughness and corrosion resistance, are easily affected by characteristics of a basic material itself. It is hence important to improve the characteristics of HAZ.

[0005] Conventionally, plain steel is employed as a basic material for a member arranged around the tire attachment area in an automobile, and the plain steel must be subjected to a coating step after welding and machining steps. The necessity of the coating step has noticeably deteriorated manufacturability and productivity.

[0006] In view of the above situation, attention has been focused on Cr-containing steel as a basic material for a member arranged around the tire attachment area in an automobile, and a variety of studies have been conducted.

[0007] In a member arranged around the tire attachment area in an automobile, stresses are apt to concentrate on a weld toe of a bead formed by MIG (Metal Inert Gas) or MAG (Metal Active Gas) welding, and the weld toe tends to become a start point of fatigue failure. For that reason, it is important to ensure mechanical characteristics, particularly strength and toughness, of an area around the weld toe, i.e., of HAZ. One example of Cr-containing steel having improved strength and toughness of a welding area is a structure-oriented martensitic stainless steel having superior weldability and workability, which is disclosed in Japanese Unexamined Patent Publication No. 55-21566. Such stainless steel has been initially studied as being employed as members arranged around the tire attachment area in an automobile.

[0008] The above-mentioned martensitic stainless steel is able to noticeably improve the toughness of HAZ by preparing a component system containing low C-low N martensite and low Ni, but cannot provide sufficient corrosion resistance of HAZ. Therefore, in spite of a parent material having superior corrosion resistance, HAZ must be coated as conventional. Eventually, a merit resulting from employing stainless steel is lessened.

[0009] As means for improving corrosion resistance of HAZ in stainless steel, it has hitherto been known with regard to ferritic stainless steel that adding Ti is effective. However, addition of Ti causes a problem in reducing the martensite phase in HAZ or lowering the strength of the martensite phase itself, thus resulting in a reduction of strength and toughness of HAZ. Note that since the strength of HAZ cannot be directly measured, it is usually determined by measuring the Vickers hardness of HAZ in accordance with the method stipulated by SAE J417, and then converting a measured result into strength.

[0010] In the state of the art, as described above, there exists no Cr-containing steel that has satisfactory levels in all of (1) toughness of HAZ, (2) strength (hardness) of HAZ, and (3) corrosion resistance of HAZ, and that is suitably used as members arranged around the tire attachment area in an automobile.

[0011] Accordingly, it is an object of the present invention to provide Cr-containing steel that has satisfactory levels in all of toughness, strength (hardness) and corrosion resistance of HAZ, and that is suitably used as parts arranged around the tire attachment area in an automobile.

DISCLOSURE OF THE INVENTION

[0012] To achieve the above object, the inventors conducted close studies on effects of various elements added in steel. As a result, the inventors found that corrosion resistance of HAZ could be noticeably improved by adding V in proper amount.

[0013] Various kinds of Cr-containing steel having different V contents on the basis of Fe-12 mass% Cr-2 mass % Mn-0.5 mass % Ni, for example, were produced by way of experiment. Each sample of the produced steel was subjected to MIG welding, and then HAZ strength (actually hardness) of each sample was measured. Also, corrosion resistance of each sample after the welding was evaluated. Obtained results are plotted in FIG. 1. The welding conditions of each sample, the method for measuring HAZ hardness, and the method for evaluating HAZ corrosion resistance were set similarly to those in Examples described later.

[0014] As seen from the results of FIG. 1, by adding V in steel in predetermined amount or more, the corrosion resistance of HAZ is noticeably improved, but the hardness is noticeably reduced when the V content exceeds 0.30 mass %.

[0015] From the above-mentioned finding, it was confirmed that, by adding V in steel in proper amount, both the hardness, i.e., the strength, and the corrosion resistance of HAZ could be obtained at high levels.

[0016] Further, it was confirmed that satisfactory toughness and strength of HAZ could be obtained by setting an F or F′ value to be not larger than a predetermined value, the F or F′ value being calculated by putting values of contents of respective components contained in steel in a formula (1) or (2) described later.

[0017] The present invention has been made on the basis of the above-mentioned findings, and the gist of the invention is as follows.

[0018] The present invention provides Cr-containing steel used for a welded structure, the steel containing, by mass %, C: not more than 0.020%, Si: not more than 1.00%, Mn: 1.0 to 5.0%, P: not more than 0.050%, S: not more than 0.020%, Cr: 6.0 to 15.0%, Ni: not more than 1.00%, Al: not more than 0.100%, N: not more than 0.020%, and V: 0.03 to 0.30%, the balance consisting of Fe and unavoidable impurities, wherein an F value calculated by putting values of contents (mass %) of the respective components in the following formula (1) is not larger than 13.50: $\begin{matrix} {{F\quad {value}} = {{Cr} + {0.4 \times {Si}} + {0.2 \times {Al}} + {5 \times P} - {0.4 \times {Mn}} - {0.7 \times {Ni}} - {35 \times C} - {10 \times N} + {10 \times V}}} & (1) \end{matrix}$

[0019] In addition, the present invention provides Cr-containing steel used for a welded structure, wherein the steel further contains Cu: not more than 2.0% and Mo: not more than 3.0%, and an F′ value calculated by putting values of contents (mass %) of the respective components in the following formula (2) is not larger than 13.50: $\begin{matrix} {{F^{\prime}\quad {value}} = {{Cr} + {0.6 \times {Mo}} + {0.4 \times {Si}} + {0.2 \times {Al}} + {5 \times P} - {0.4 \times {Mn}} - {0.7 \times {Ni}} - {0.6 \times {Cu}} - {35 \times C} - {10 \times N} + {10 \times V}}} & (2) \end{matrix}$

[0020] Moreover, the present invention provides Cr-containing steel used for a welded structure, wherein the steel further contains B: 0.0003 to 0.0050% by mass %.

BRIEF DESCRIPTION OF THE DRAWINGS

[0021]FIG. 1 is a graph plotting hardness and corrosion resistance of HAZ versus V content (mass %) in Cr-containing steel that contains Fe-12 mass % Cr-2 mass % Mn-0.5 mass % Ni as basic components.

[0022]FIG. 2 is an illustration showing positions at which HAZ hardness was measured.

[0023]FIG. 3 is an illustration showing a position at which a Charpy impact test piece was sampled.

[0024]FIG. 4 is an illustration showing a test piece sampled for a salt-spray test.

BEST MODE OF CARRYING OUT THE INVENTION

[0025] The reasons why the contents of components of Cr-containing steel according to the present invention (referred to simply as “inventive steel” hereinafter) are limited to the above-mentioned ranges will be described below in detail.

[0026] C: not more than 0.020 mass % and N: not more than 0.020 mass %

[0027] In the inventive steel, C and N are components adversely affecting corrosion resistance of HAZ. If any of the contents of C and N in the steel exceeds 0.020 mass %, the corrosion resistance is noticeably deteriorated. Therefore, the contents of C and N are both set to be not more than 0.020 mass %.

[0028] Additionally, for increasing strength (hardness) of HAZ, C and N are both preferably not less than 0.005 mass %.

[0029] Si: 0.05 mass % to 1.00 mass %

[0030] Si has a deoxidizing action and is a component essential from the viewpoint of steel-making. Therefore, Si of not less than 0.05 mass % is usually contained in molten steel after the steel-making process. If the Si content exceeds 1.00 mass % in the component system of the present invention, the martensite phase produced in HAZ would be noticeably reduced. Accordingly, the Si content is limited to be not more than 1.00 mass %.

[0031] Mn: 1.0 to 5.0 mass %

[0032] Mn is a component essential for stabilizing the γ (austenite) phase at high temperature and achieving satisfactory hardenability. Therefore, a lower limit of the Mn content is set to 1.0 mass %. On the other hand, if the Mn content exceeds 5.0 mass %, toughness of HAZ would be deteriorated. Accordingly, an upper limit of the Mn content is set to 5.0 mass %.

[0033] P: not more than 0.050 mass %

[0034] The P content is preferably as low as possible from the viewpoint of workability. However, from the viewpoint of economic restriction imposed on the dephosphorizing process in steel-making, an upper limit of the P content is set to 0.050 mass %.

[0035] S: not more than 0.020 mass %

[0036] The S content is preferably as low as possible from the viewpoint of corrosion resistance. However, from the viewpoint of economic restriction imposed on the desulfurizing process in steel-making, an upper limit of the S content is set to 0.020 mass %.

[0037] Cr: 6.0 to 15.0 mass %

[0038] Cr is a component effective in improving corrosion resistance. When the Cr content is set to be not less than 6.0 mass %, the corrosion resistance is noticeably improved, and hence a lower limit of the Cr content is set to 6.0 mass %. On the other hand, if the Cr content exceeds 15.0 mass %, a larger amount of Ni would be required to produce the martensite phase in HAZ and the cost would be increased. Therefore, an upper limit of the Cr content is set to 15.0 mass %. Preferably, the Cr content is set to the range of 10.0 to 15.0 mass %.

[0039] Ni: 0.10 to 1.00 mass %

[0040] Ni is a component for stabilizing the γ phase at high temperature. To develop the stabilizing effect, Ni requires to be added in amount not less than 0.10 mass %. However, Ni is expensive and positive addition of Ni increases the cost. Accordingly, an upper limit of the Ni content is set to 1.00 mass %.

[0041] Al: not more than 0.100 mass %

[0042] Al is an essential component serving as a deoxidizer from the viewpoint of steel-making. Therefore, Al of not less than 0.02 mass % is usually contained in molten steel after the steel-making process. However, when Al is not used as a deoxidizer, it is usual that Al of not less than 0.002 mass % is unavoidably contained. If Al is overly added in excess of 0.100 mass %, inclusions are more apt to generate and toughness tends to deteriorate. Accordingly, an upper limit of the Al content is set to 0.100 mass %.

[0043] V: 0.03 to 0.30 mass %

[0044] V is a component effective in improving corrosion resistance of HAZ when added in steel in proper amount. The effect is developed at the V content of not less than 0.03 mass %, but if V is overly added in excess of 0.30 mass %, strength and toughness of HAZ would be deteriorated. Therefore, the V content is set to the range of 0.03 to 0.30 mass %. For satisfying both the corrosion resistance and strength (hardness) of HAZ at high levels, the V content is preferably set to the range of 0.06 to 0.15 mass %.

[0045] In the present invention, for ensuring satisfactory toughness and strength (hardness) of HAZ, it is an essential feature in addition to the above-described limitations of steel composition that an F value calculated by putting values of contents (mass %) of the respective components in the following formula (1) is not larger than 13.50: $\begin{matrix} {{F\quad {value}} = {{Cr} + {0.4 \times {Si}} + {0.2 \times {Al}} + {5 \times P} - {0.4 \times {Mn}} - {0.7 \times {Ni}} - {35 \times C} - {10 \times N} + {10 \times V}}} & (1) \end{matrix}$

[0046] In the above formula (1), Cr, Si, Al, P and V are the so-called ferrite generating elements and impede generation of the γ phase at high temperature. On the other hand, Mn, Ni, C and N are the so-called austenite generating elements and promote generation of the γ phase at high temperature. It was found that an increase of the F value made it harder to generate the γ phase at high temperature and to obtain toughness and strength of HAZ at sufficient levels. As a result of conducting closer studies, it was also found that, by setting the F value to be not larger than 13.50, fine and soft martensite phase was precipitated in HAZ and sufficient levels of toughness and strength were ensured in a welding area.

[0047] For those reasons, the F value is limited to be not larger than 13.50 in the component system of the present invention.

[0048] Thus, by employing the features set forth above, the present invention has succeeded in developing Cr-containing steel that has satisfactory levels in all of toughness, strength (hardness) and corrosion resistance of HAZ, and that is suitably used as, in particular, parts arranged around the tire attachment area in an automobile.

[0049] Also, in the present invention, Cu and Mo may be added in the steel as other suitable components if necessary.

[0050] Cu: 0.10 to 2.00 mass %

[0051] Cu is a component effective in not only improving corrosion resistance, but also stabilizing the γ phase at high temperature. To develop those effects, Cu is required to be added in amount not less than 0.10 mass %. However, if Cu is overly added in excess of 2.00 mass %, hot workability of the steel would be deteriorated. Therefore, an upper limit of the Cu content is set to 2.00 mass %. Preferably, the Cu content is set to be not more than 1.00 mass %.

[0052] Mo: 0.40 to 3.00 mass %

[0053] Mo is a component effective in improving corrosion resistance. To develop that effect, Mo is required to be added in amount not less than 0.40 mass %. However, if Mo is overly added in excess of 3.00 mass %, the basic material would be embrittled because Mo is the ferrite generating element. Therefore, an upper limit of the Mo content is set to 3.00 mass %.

[0054] In the component system containing Cu and Mo in the steel, it is an essential feature that, instead of the F value, an F′ value calculated by putting values of contents (mass %) of the respective components in the following formula (2), in which the contents of both Cu and Mo components are taken into account, is not larger than 13.50: $\begin{matrix} {{F^{\prime}\quad {value}} = {{Cr} + {0.6 \times {Mo}} + {0.4 \times {Si}} + {0.2 \times {Al}} + {5 \times P} - {0.4 \times {Mn}} - {0.7 \times {Ni}} - {0.6 \times {Cu}} - {35 \times C} - {10 \times N} + {10 \times V}}} & (2) \end{matrix}$

[0055] In the Cr-containing steel described above, B may be added in the steel if necessary.

[0056] B: 0.0003 to 0.0050 mass %

[0057] B is a component effective in improving hardenability, increasing hardness of HAZ, as well as suppressing cracks due to embrittlement. Those effects are developed at the B content of not less than 0.0003 mass %, but if the B content exceeds 0.0050 mass %, toughness would be deteriorated. Therefore, the B content is set to the range of 0.0003 to 0.0050 mass %. Preferably, the B content is set to the range of 0.0005 to 0.0015%.

[0058] A method for manufacturing the Cr-containing steel according to the present invention is not limited to a particular one. For example, the method that is generally employed in manufacturing Cr-containing steel, such as stainless steel, may be applied substantially as it is. One example of the manufacturing method will be described below.

[0059] A basic steel material obtained through continuous casting is first heated up to a predetermined temperature as required. The basic steel material is then subjected to hot rolling, whereby a hot-rolled plate having a desired plate thickness is obtained. Subsequently, the hot-rolled plate is subjected to box annealing at 600 to 900° C. depending on a required strength level, and it is brought into practical use as it is or after pickling. Otherwise, the annealed plate is subjected to cold rolling, whereby a cold-rolled plate having a predetermined thickness is obtained. Then, the cold-rolled plate is subjected to continuous annealing at preferably 700 to 900° C. and pickling. As a result, Cr-containing steel is manufactured in the form of a cold-rolled and annealed plate.

[0060] Note that the above-described manufacturing process merely represents one example of embodiments of the present invention, various processes can be added depending on applications.

EXAMPLES

[0061] The present invention will be described below in more detail in connection with Examples of the invention and Comparative Examples.

[0062] A hot-rolled plate having a thickness of 4 mm was produced by smelting 50 kg of a steel ingot having the chemical composition, shown in Table 1, in a vacuum smelting furnace, and hot-rolling the ingot under ordinary hot-rolling conditions. Then, the hot-rolled plate was annealed at 700° C.×8 hours and subjected to MIG welding under conditions given below. Subsequently, the welded plate was evaluated for not only Vickers hardness as evaluation of HAZ hardness, but also toughness and corrosion resistance of HAZ.

Welding Conditions

[0063] Butt Welding

[0064] Welding Wire: wire diameter 1.2 mmφ, material: SUS309S (JIS G4309)

[0065] Shield Gas: 95 vol. % Ar-5% vol. % Oxygen

[0066] Welding Current: 170 A, Welding Voltage: 24 V,

[0067] Welding Rate: 400 mm/min

[0068] (1) Method for Measuring HAZ Hardness

[0069] Hardness of HAZ was measured in accordance with the Vickers hardness testing method stipulated by JIS (Japanese Industrial Standard) Z 2244-1992. A test load was set to 9.8 N (1 kgf), and the HAZ hardness was measured at three positions (spaced from each other at a pitch of 0.8 mm) shown in FIG. 2. The HAZ hardness was evaluated based on an average of the measured hardness values. The measured results are listed in Table 1.

[0070] (2) Method for Evaluating HAZ Toughness

[0071] Toughness of HAZ was evaluated as follows. Three No. 4 test pieces stipulated by JIS Z 2202-1980 were each sampled from a position shown in FIG. 3 (each of the test pieces being a sub-size test piece finished to have a thickness of 2 mm by cutting and grinding the front and rear sides of the test piece, and having a 2-mm V-notch formed in a HAZ position to extend parallel to the welding direction). Each test piece was set on a Charpy impact tester and then tested in accordance with the Charpy impact testing method stipulated by JIS Z 2242-1993. Energy absorbed in the test for breaking the test piece was calculated, and the HAZ toughness was evaluated based on an average of absorbed energy values obtained from three test pieces. Incidentally, the test temperature was set to 0° C. The absorbed energy value calculated for each type of test piece was listed in Table 1.

[0072] (3) Method for Evaluating HAZ Corrosion Resistance

[0073] Corrosion resistance of HAZ was evaluated as follows. After welding, two samples having a size of 60 mm×80 mm were each cut out from a position shown in FIG. 4. After polishing an area of a 20-mm width on the rear side of each test piece, including a weld, with a #400 sandpaper, a salt-spray test (SST) was performed on the test piece for 4 hours in accordance with JIS Z 2371. The corrosion resistance of HAZ was evaluated by regarding an area of a 10-mm width including a welded bead at the center as HAZ (10 mm×80 mm), and then measuring the size of a rusty area in HAZ. The evaluated results are listed in Table 1. In table 1, a mark “◯” represents the case in which the rusty area given as an average obtained from the two samples is 5% (rusty area of 40 mm²/HAZ area of 800 mm²) or less. A mark “Δ” represents the case in which the rusty area given as an average obtained from the two samples is in the range of 5% to 50% (rusty area of 40 mm² to 400 mm²). A mark “X” represents the case in which the rusty area given as an average obtained from the two samples was over 50% (rusty area of 400 mm² or over).

[0074] As seen from the results of Table 1, in inventive steels 1 to 3 and 10 in which a proper amount of V is added, the corrosion resistance of HAZ is noticeably superior to that of comparative steels A and B in which the V content in the steel deviates from the proper range in the present invention. Also, it is seen that, in inventive steels 4 and 5, since B is further added in the steel within a preferred range of content, hardenability is improved and hence the hardness of HAZ is increased correspondingly. In inventive steels 6 to 9 and 11, since at least one of Mo and Cu is further added in the steel within a preferred range of content, the effects of reducing a pit depth and improving the corrosion resistance in comparison with the case of adding neither Mo nor Cu are obtained. Hence, satisfactory levels are achieved in all of toughness, hardness and corrosion resistance of HAZ.

[0075] On the other hand, in a comparative steel C, since V is added in the steel over the proper range in the present invention, both the hardness and toughness of HAZ are deteriorated. In a comparative steel D, since Mn is added in the steel over the proper range in the present invention, the toughness of HAZ is deteriorated. In a comparative steel E, since the F value exceeds the proper range in the present invention, the toughness of HAZ is deteriorated.

Industrial Applicability

[0076] Since the Cr-containing steel according to the present invention is superior in all of toughness, strength (hardness) and corrosion resistance of HAZ, it can be used for a welded structure, particularly it is suitably used as members arranged around the tire attachment area in an automobile.

[0077] Note that the Cr-containing steel according to the present invention can be used in any desired form such as a pipe and plate. While Examples of the present invention were described in connection with the case of employing a hot-rolled plate, similar advantages are also obtained in the case of employing a cold-rolled plate. Further, the Cr-containing steel according to the present invention may be used after coating, as required, for the purpose of further improving the corrosion resistance of HAZ, and such a case also falls within the scope of the present invention. TABLE 1 F OR STEEL CHEMICAL COMPOSITION (mass %) F′ No. C Si Mn P S Cr Ni Al N V B Mo Cu VALUE T U W REMARKS 1 0.008 0.15 1.5 0.012 0.003 12.0 0.54 0.005 0.007 0.08 — — — 11.59 253 295 ∘ INVENTIVE 2 0.011 0.15 1.5 0.020 0.003 11.5 0.64 0.01 0.008 0.12 — — — 11.35 260 280 ∘ STEEL 3 0.008 0.18 1.6 0.023 0.002 11.2 0.26 0.02 0.009 0.30 — — — 13.20 289 265 ∘ 4 0.010 0.16 1.5 0.011 0.003 11.8 0.55 0.02 0.015 0.12 0.0008 — — 11.64 250 305 ∘ 5 0.009 0.18 1.5 0.022 0.004 11.9 0.45 0.05 0.008 0.12 0.0015 — — 11.98 265 315 ∘ 6 0.009 0.15 2.8 0.019 0.005 14.8 0.81 0.08 0.009 0.08 — — 0.45 13.41 200 260 ∘ 7 0.004 0.27 1.5 0.033 0.003 10.8 0.35 0.005 0.009 0.06 0.0015 0.48 0.35 10.68 253 305 ∘ 8 0.015 0.08 2.0 0.011 0.018 12.3 0.95 0.005 0.015 0.12 0.0009 1.25 0.31 12.01 223 325 ∘ 9 0.011 0.08 2.0 0.012 0.005 14.8 0.88 0.02 0.015 0.05 0.0014 0.48 0.56 13.40 170 335 ∘ 10 0.002 0.15 2.5 0.024 0.005 12.3 0.67 0.04 0.002 0.12 — — — 12.13 200 250 ∘ 11 0.008 0.45 1.4 0.012 0.003  9.5 0.54 0.005 0.007 0.13 — 1.5 0.5 10.35 305 300 ∘ A 0.011 0.18 1.5 0.031 0.006 10.9 0.31 0.02 0.018 0 — — — 9.75 230 320 x COMPARA- B 0.018 0.16 1.4 0.036 0.004 11.0 0.41 0.04 0.018 0.02 — — — 9.80 240 320 Δ TIVE C 0.004 0.15 2.2 0.028 0.003 11.1 0.99 0.03 0.009 0.38 — — — 13.30 58 180 ∘ STEEL D 0.004 0.35 5.6 0.018 0.010 11.5 0.15 0.02 0.008 0.15 — — — 10.67 100 280 ∘ E 0.007 0.16 1.5 0.032 0.008 14.5 0.12 0.03 0.005 0.15 — — — 15.25 68 200 ∘ 

1. Cr-containing steel used for a welded structure, the steel containing, by mass %, C: not more than 0.020%, Si: not more than 1.00%, Mn: 1.0 to 5.0%, P: not more than 0.050%, S: not more than 0.020%, Cr: 6.0 to 15.0%, Ni: 0.10 to 1.00% or less, Al: not more than 0.100%, N: not more than 0.020%, and V: 0.03 to 0.30%, the balance consisting of Fe and unavoidable impurities, wherein an F value calculated by putting values of contents of the respective components in the following formula (1) is not larger than 13.50: $\begin{matrix} {{F\quad {value}} = {{Cr} + {0.4 \times {Si}} + {0.2 \times {Al}} + {5 \times P} - {0.4 \times {Mn}} - {0.7 \times {Ni}} - {35 \times C} - {10 \times N} + {10 \times {V.}}}} & (1) \end{matrix}$


2. Cr-containing steel used for a welded structure according to claim 1, wherein the steel further contains Cu: 0.10 to 2.00% and Mo: 0.40 to 3.00%, the balance consisting of Fe and unavoidable impurities, and an F′ value calculated by putting values of contents of the respective components in the following formula (2) is not larger than 13.50: $\begin{matrix} {{F^{\prime}\quad {value}} = {{Cr} + {0.6 \times {Mo}} + {0.4 \times {Si}} + {0.2 \times {Al}} + {5 \times P} - {0.4 \times {Mn}} - {0.7 \times {Ni}} - {0.6 \times {Cu}} - {35 \times C} - {10 \times N} + {10 \times {V.}}}} & (2) \end{matrix}$


3. Cr-containing steel used for a welded structure according to claim 1 or 2, wherein the steel further contains B: 0.0003 to 0.0050% by mass %.
 4. Cr-containing steel used for a welded structure according to any one of claims 1 to 4, wherein the Cr-containing steel is a hot-rolled plate.
 5. Cr-containing steel used for a welded structure according to any one of claims 1 to 4, wherein the Cr-containing steel is a cold-rolled plate subjected to cold rolling after hot rolling. 